PS 9020R
PS, 100% PCR, Household Appliances Source, Colorable, Injection Molding.
| Properties | Test Condition | Typical Value | Unit | Test Standard |
| Mechanical | ||||
| Tensile Strength | 50mm/min | ＞20 | MPa | ASTM D638 |
| Tensile Strain at Break | 50mm/min | ＞20 | % | ASTM D638 |
| Flexural Strength | 5mm/min | 1600~2600 | MPa | ASTM D790 |
| Flexural Modulus | 5mm/min | ＞35 | MPa | ASTM D790 |
| Izod Notched Impact Strength | 3.18mm | ＞60 | J/m | ASTM D256 |
| Physical | ||||
| Density | 23oC | 1.05-1.08 | g/cm3 | ASTM D792 |
| Melt Flow Index | 200 oC, 5kg | 3~9 | g/10min | ASTM D1238 |
| Molding Shrinkage | – | 0.5~0.7 | % | ASTM D955 |
| Flammability | ||||
| Flame Rating | 1.6mm | HB | – | UL 94 |
TypicalProcessing Conditions
| Range (Optimum) | unit | |
| Pre-dry Temperature | 70-80 | oC |
| Pre-dry Time | 2-4 | hrs |
| Melt Temperature | 200-240 | oC |
| Rear Temperature | 180-210 | oC |
| Middle Temperature | 190-220 | oC |
| Front Temperature | 200-240 | oC |
| Mold Temperature | 30-80 | oC |
The listed values are maybe different for pigmented material.