PC 1020-12B – CTC-CARBONEU

PC 1020-12B

PC, 100% PCR, Water Bottle Source, High Viscosity, Colorable, Extrusion/Injection Molding.

Properties	Test Condition	Typical Value	Unit	Test Standard
Mechanical
Tensile Strength	50mm/min	61	MPa	ASTM D638
Tensile Strain at Break	50mm/min	＞50	%	ASTM D638
Flexural Strength	5mm/min	2000	MPa	ASTM D790
Flexural Modulus	5mm/min	89	MPa	ASTM D790
Izod Notched Impact Strength	3.18mm	650	J/m	ASTM D256
Physical
Density	23^oC	1.20	g/cm³	ASTM D792
Melt Flow Index	300^oC, 1.2kg	10~14	g/10min	ASTM D1238
Molding Shrinkage	–	0.5~0.7	%	ASTM D955
Flammability
Flame Rating	1.6mm	HB	–	UL 94
Thermal
Temperature of Deflection Under Load	1.8MPa	125	^oC	ASTM D648
Optical Others
Visible Transmittance	1mm	60~70	%	ASTM D1003
Appearance/ L*	Penetration D65/10 1mm	75~80	–	Internal Method
Appearance/ a*	Penetration D65/10 1mm	-6.0~-2.0	–	Internal Method
Appearance/ b*	Penetration D65/10 1mm	-4.0~-2.0	–	Internal Method

TypicalProcessing Conditions

	Range (Optimum)	unit
Pre-dry Temperature	110-120	^oC
Pre-dry Time	2-4	hrs
Melt Temperature	280-320	^oC
Rear Temperature	270-300	^oC
Middle Temperature	280-310	^oC
Front Temperature	280-320	^oC
Mold Temperature	90-120	^oC

*These are typical values of the product’s properties, and these values alone do not represent a sufficient basis for any part design and are not intended for use in not the permit of quality assurance.
The listed values are maybe different for pigmented material.