PCABS 3026-C13R50 – CTC-CARBONEU

PCABS 3026-C13R50

PC/ABS Blend, 50% PCR, 13% Mineral Filled, Halogen-Free Flame Retardant, High Modulus, Injection Molding.

Properties	Test Condition	Typical Value	Unit	Test Standard
Mechanical
Tensile Strength	50mm/min	67	MPa	ASTM D638
Tensile Strain at Break	50mm/min	18	%	ASTM D638
Flexural Strength	5mm/min	4300	MPa	ASTM D790
Flexural Modulus	5mm/min	98	MPa	ASTM D790
Izod Notched Impact Strength	3.18mm	100	J/m	ASTM D256
Physical
Density	23^oC	1.28	g/cm³	ASTM D792
Melt Flow Index	240^oC, 5kg	17	g/10min	ASTM D1238
Molding Shrinkage	–	0..3-0.5	%	ASTM D955
Flammability
Flame Rating	–	V0	–	UL 94
Thermal
Temperature of Deflection Under Load	1.8MPa	86	^oC	ASTM D648

TypicalProcessing Conditions

	Range (Optimum)	unit
Pre-dry Temperature	80-90	^oC
Pre-dry Time	4-6	hrs
Melt Temperature	220-240	^oC
Rear Temperature	240-260	^oC
Middle Temperature	245-265	^oC
Front Temperature	250-270	^oC
Mold Temperature	60-100	^oC

*These are typical values of the product’s properties, and these values alone do not represent a sufficient basis for any part design and are not intended for use in not the permit of quality assurance.
The listed values are maybe different for pigmented material.