PCABS 3027R70
PC/ABS Blend, 70% PCR, Halogen-Free Flame Retardant, High Impact, Injection Molding.
| Properties | Test Condition | Typical Value | Unit | Test Standard |
| Mechanical | ||||
| Tensile Strength | 50mm/min | 61 | MPa | ASTM D638 |
| Tensile Strain at Break | 50mm/min | 90 | % | ASTM D638 |
| Flexural Strength | 5mm/min | 2200 | MPa | ASTM D790 |
| Flexural Modulus | 5mm/min | 92 | MPa | ASTM D790 |
| Izod Notched Impact Strength | 3.18mm | 660 | J/m | ASTM D256 |
| Physical | ||||
| Density | 23oC | 1.18 | g/cm3 | ASTM D792 |
| Melt Flow Index | 240 oC, 5kg | 19 | g/10min | ASTM D1238 |
| Molding Shrinkage | – | 0.4-0.6 | % | ASTM D955 |
| Flammability | ||||
| Flame Rating | 1.2mm | V0 | – | UL 94 |
| Thermal | ||||
| Temperature of Deflection Under Load | 1.8MPa | 85 | oC | ASTM D648 |
TypicalProcessing Conditions
| Range (Optimum) | unit | |
| Pre-dry Temperature | 80-90 | oC |
| Pre-dry Time | 4-6 | hrs |
| Melt Temperature | 220-240 | oC |
| Rear Temperature | 240-260 | oC |
| Middle Temperature | 245-265 | oC |
| Front Temperature | 250-270 | oC |
| Mold Temperature | 60-100 | oC |
The listed values are maybe different for pigmented material.