PC 1026R50
Modified PC, 50% PCR, Halogen Free Flame Retardant, Heat Resistance, High Impact, Injection Molding.
| Properties | Test Condition | Typical Value | Unit | Test Standard |
| Mechanical | ||||
| Tensile Strength | 50mm/min | 650 | MPa | ASTM D638 |
| Tensile Strain at Break | 50mm/min | 100 | % | ASTM D638 |
| Flexural Strength | 5mm/min | 21000 | MPa | ASTM D790 |
| Flexural Modulus | 5mm/min | 920 | MPa | ASTM D790 |
| Izod Notched Impact Strength | 3.18mm | 72 | J/m | ASTM D256 |
| Physical | ||||
| Density | 23oC | 1.20 | g/cm3 | ASTM D792 |
| Melt Flow Index | 300 oC, 1.2kg | 10 | g/10min | ASTM D1238 |
| Molding Shrinkage | – | 0.2-0.4 | % | ASTM D955 |
| Flammability | ||||
| Flame Rating | 1.0mm | V0 | – | UL 94 |
| Thermal | ||||
| Temperature of Deflection Under Load | 1.8MPa | 125 | oC | ASTM D648 |
TypicalProcessing Conditions
| Range (Optimum) | unit | |
| Pre-dry Temperature | 110-120 | oC |
| Pre-dry Time | 2-4 | hrs |
| Melt Temperature | 280-320 | oC |
| Rear Temperature | 270-300 | oC |
| Middle Temperature | 280-310 | oC |
| Front Temperature | 280-320 | oC |
| Mold Temperature | 60-110 | oC |
The listed values are maybe different for pigmented material.