PC 1022-C20R30 – CTC-CARBONEU

PC 1022-C20R30

Modified PC, 30% PCR, 20% Glass Fiber Filled, High Stiffness, Injection Molding.

Properties	Test Condition	Typical Value	Unit	Test Standard
Mechanical
Tensile Strength	50mm/min	95	MPa	ASTM D638
Tensile Strain at Break	50mm/min	3.5	%	ASTM D638
Flexural Strength	5mm/min	5000	MPa	ASTM D790
Flexural Modulus	5mm/min	150	MPa	ASTM D790
Izod Notched Impact Strength	3.18mm	160	J/m	ASTM D256
Physical
Density	23^oC	1.32	g/cm³	ASTM D792
Melt Flow Index	300^oC, 1.2kg	12	g/10min	ASTM D1238
Molding Shrinkage	–	0.2-0.4	%	ASTM D955
Flammability
Flame Rating	1.6mm	HB	–	UL 94
Thermal
Temperature of Deflection Under Load	1.8MPa	136	^oC	ASTM D648

TypicalProcessing Conditions

	Range (Optimum)	unit
Pre-dry Temperature	110-120	^oC
Pre-dry Time	4-6	hrs
Melt Temperature	280-320	^oC
Rear Temperature	270-300	^oC
Middle Temperature	280-310	^oC
Front Temperature	280-320	^oC
Mold Temperature	60-120	^oC

*These are typical values of the product’s properties, and these values alone do not represent a sufficient basis for any part design and are not intended for use in not the permit of quality assurance.
The listed values are maybe different for pigmented material.