PA6 4020R
PET, OBP, Fishing Net Source, Injection/Extrusion Molding.
| Properties | Test Condition | Typical Value | Unit | Test Standard |
| Mechanical | ||||
| Tensile Strength | 50mm/min | 70 | MPa | ASTM D638 |
| Tensile Strain at Break | 50mm/min | ＞10 | % | ASTM D638 |
| Flexural Strength | 5mm/min | 3400 | MPa | ASTM D790 |
| Flexural Modulus | 5mm/min | 100 | MPa | ASTM D790 |
| Izod Notched Impact Strength | 3.18mm | 100 | J/m | ASTM D256 |
| Physical | ||||
| Density | 23oC | 1.12 | g/cm3 | ASTM D792 |
| Molding Shrinkage | – | 1.0-1.4 | % | ASTM D1238 |
| Flammability | ||||
| Flame Rating | – | HB | – | UL 94 |
TypicalProcessing Conditions
| Range (Optimum) | unit | |
| Pre-dry Temperature | 110-120 | oC |
| Pre-dry Time | 2-4 | hrs |
| Melt Temperature | 280-320 | oC |
| Rear Temperature | 270-300 | oC |
| Middle Temperature | 280-310 | oC |
| Front Temperature | 280-320 | oC |
| Mold Temperature | 90-120 | oC |
The listed values are maybe different for pigmented material.